Injection molding products in the product molding is not complete reasons: This is a frequently encountered problem, but also easier to solve. When the technology can not be resolved with the means, from the mold design and manufacturing to consider improving, generally can be resolved.

First, the equipment:

1. Plastic injection molding machine is small. When the quality of the product exceeds the actual maximum injection quality of the injection molding machine, it is clear that the amount of feed is made better. If the quality of the product is close to the actual injection molding quality of the injection molding machine, there is a problem that the plasticization is not sufficient and the heating time in the barrel is insufficient. As a result, the appropriate melt can not be supplied to the mold in time. This situation only to replace the large capacity of the injection molding machine to solve the problem. Some plastics such as nylon (especially nylon 66) melting range is narrow, the greater the specific heat, the need for plasticizing capacity of the injection molding machine to ensure the supply of materials.

2. Thermometer shows the temperature is not real, bright high real low, causing the material temperature is too low. This is due to temperature control devices such as thermocouple and its line or temperature millivolt failure, or because the distance from the heating point of the electric ring aging or burning, heating failure and never found or no timely repair replacement.

3. The nozzle bore diameter is too large or too small. It is too small, because the flow diameter is small, the specific volume of the material increases, easy to chill, plug the feed channel or consume the injection pressure; too large, the flow cross-sectional area, the plastic mold per unit area pressure is low A small situation. At the same time, non-Newtonian plastics such as ABS do not get a large shear heat and can not make the viscosity drop caused by filling difficult.

Nozzle and the main channel entrance with the bad, often occur outside the mold material, mold filled with dissatisfaction with the phenomenon. The nozzle itself or the main channel entrance spherical damage, deformation, and the impact of good cooperation with each other; Note mechanical failure or deviation, so that the nozzle and the main channel axis to produce tilt Displacement or axial compression surface detachment; nozzle diameter than the main channel inlet ball diameter, due to the edge of the gap, in the flash material squeeze gradually increase the axial thrust of the nozzle will cause the product note dissatisfaction.

4. Plastic frit blockage feed channel. As the plastic in the hopper dryer local melting agglomeration, or barrel feed section temperature is too high, or improper choice of plastic grade, or plastic containing too much lubricant will make the plastic into the feed port diameter position or screw From the screw deep groove within the premature melting, aggregates and fritters bonded to each other to form a "bridge", plug the channel or wrap the screw, with the screw rotation for circumferential sliding, can not move forward, resulting in material interruption or irregular fluctuations The This situation is only in the chisel channel, excluding the block before they can be fundamentally resolved.

5. nozzle cold material into the mold. Injection molding machines are usually fitted with straight through nozzles due to pressure loss. However, if the barrel front and nozzle temperature is too high, or in the high pressure state of the front end of the barrel material is too much, resulting in "salivation", so that the plastic injection of the mold and open the case, accidentally first into the main channel entrance In the cooling effect of the template hardened, and hinder the smooth melt into the cavity. At this time, should reduce the barrel front and nozzle temperature and reduce the barrel of the storage capacity, reduce the back pressure to prevent the front end of the barrel melt density is too large.

6. Injection cycle is too short. As the cycle is short, the temperature is too late to keep up with the lack of material, when the voltage fluctuation is particularly evident. According to the supply voltage to adjust the cycle accordingly. Adjustment generally do not consider the injection and packing time, the main consideration from the completion of the adjustment to the screw back to the period of time, does not affect the filling molding conditions, but also to extend or shorten the grain in the barrel of the warm-up time.


keyworks:

底部

ZHONGZHOU

zhongzhou Garden Machinery

focus on R&D、producing and selling
a professional manufacturer

Tel:0579-87158009

E-mail:simon@ykzhongzhou.com

NEWS

    PRODUCTS

    Our main products cover nylon trimmer line,trimmer head,brush cutter gear case assy,clutch case assy...

    Scan QR code

    Scan QR code

    All rights reserved: Yongkang Zhongzhou Garden Machinery Co., Ltd
    Message